1. Mixing of the two components

Mix Part A and Part B components according to recommended weight ratios.

The materials can be processed differently according to the version:

BLUESIL ESA 6110 A&B

Hand mixing: The two components are thoroughly mixed using an electrical or pneumatic

mixer, on a low speed setting so as to limit the inclusion of air in the mixture. A dispensing

machine can also be used.

After mixing A and B parts, it is preferable to degas the product to eliminate the air

bubbles that would be visible in the finished part and which would reduce the

mechanical and dielectric properties.

Degassing is generally carried out with a vacuum of 30 to 50 mbar releasing the

vacuum several times during the operation. A recipient with a high diameter/height ratio

is better suited to quick degassing; however the height must be sufficient to contain the

swelling of the elastomer under vacuum conditions.

Automatic mixing: A dispensing machine can also be used (refer to procedure

recommended for BLUESIL ESA 6110 QC A&B).

BLUESIL ESA 6110 QC A&B

The products should only be used by means of automatic dosing equipment with a

meter/static mixer, as the pot life is too short to hand-mix and efficiently degas the

material.

Automatic mixing: In order to avoid any air bubbles that may affect the mechanical and

dielectric properties, it is recommended to degas separately A and B part, prior to pour

it slowly and regularly into the tanks of the dosing machine. The A and B Parts should

be dosed and mixed with a static mixer with a standard commercial equipment (A

special care is recommended in pumping the product from the tanks to avoid any air

entry before dosing and mixing).

2. After mixing

BLUESIL ESA 6110 A&B or BLUESIL ESA 6110 QC A&B are poured slowly and

regularly. In the case of a high thickness potting operation, it must be made at the

lowest point in the volume to be filled; this avoids forming and including air bubbles in

the volume. It should not be filled totally to allow expansion of the mixture at service

temperatures.

Certain materials that the BLUESIL ESA 6110 A&B and BLUESIL ESA 6110 QC

A&B may be in contact with when curing could inhibit the reaction. Especially

troublesome materials are: sulphur-containing cured natural and synthetic rubber

compounds (neoprene, latex, SBR), tin catalyzed silicone rubbers, amine

catalyzed epoxies, PVC stabilized with tin salts and some polyurethane

elastomers.

STORAGE -10°C < t < +30°C IN ITS ORIGINAL PACK STIR WELL BEFORE USEStore in a cool, dry place with adequate ventilation. Keep away from incompatible materials, open flames, and high temperatures. Store in original tightly closed container. Suitable containers: polyethylene. Steel drums coated with epoxy-resin.Please consult the Safety Data Sheet of this product.RoHS;VOC;WEEE

BLUESIL ESA 6110 B

BLUESIL ESA 6110 A&B is a pourable, two component silicone rubber that cures at room temperature by a polyaddition reaction, to a very soft and optical clear silicone gel.

BLUESIL ESA 6110 A&B is particularly recommended for high transparency applications.

A quick curing version, BLUESIL ESA 6110 QC A&B is also available.

Optical Encapsulant;Optical Transparency;Protection;UV resistant

2 Part RTV

Fluid

RoHS;VOC;WEEE

  • Easy processing, due to the good fluidity of parts A and B and their mixing ratio (1:1).
  • Good pourability.
  • Optically clear.
  • Quick setting, accelerated by heating.
  • Pronounced inherent tack.
  • Outstanding dielectric properties.
  • Good heat stability in confined space (even above 100°C).
  • Outstanding protection of encapsulated equipment against mechanical stress due to temperature variations and vibrations.
  • Protection of electronic units by potting.
  • Encapsulation of electronic components, sensors for the automotive and power electronics industries.
  • Encapsulation of solar cells.
  • Damping systems.

Asia Pacific;Europe Middle East Africa;Central and South America;North America

For information about Storage and Shelf Life for this product, please download the Technical Data Sheet.

 Characteristics_A

 

 

Viscosity1200PairedCompISO 3219mPa.s

 Characteristics_B

 

 

Viscosity1000PairedCompISO 3219mPa.s

 

 

 Table_Characteristics_A_And_B

 

 

penetration_a142c699-2b17-4f82-882a-75f6253332edpenetration_a142c699-2b17-4f82-882a-75f6253332edPenetration250PairedMixISO 21371/10mm
pot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6apot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6aPot life50PairedMixmin
working-time_ea6d5b8a-5ff3-4b13-996b-45964448efa5working-time_ea6d5b8a-5ff3-4b13-996b-45964448efa5Working Time50PairedMixmin

 

 

 

 

BLUESIL ESA 6110 ABLUESIL ESA 6110 A/our_offer/Product/90058441/90058442/BLUESIL-ESA-6110-A

 

 

 

 

 NeedAnExpert

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

Adhesive Silicones Solutionshttps://www.bluestarsilicones.com/EN/Our_offer/KEC/ListInstance_Brochure_Title/AdhesiveSiliconesSolutions_Brochure.pdfAdhesive Silicones Solutions

 TDS

 

 

 

 

 

 

BLUESIL ESA 6110 QC BBLUESIL ESA 6110 QC B/our_offer/Product/90059088/90059087/BLUESIL-ESA-6110-QC-B

 SQUARE_NEWS_EVENT_PRODUCT