1. Mixing of the two components
Add 100 parts of BLUESIL RTV 3542 A to 100 parts of BLUESIL RTV 3542 B. The two components may be intimately mixed either by hand or using a low-speed electric or pneumatic mixer to minimize the introduction of air into the mixture.

2. Degassing
After mixing parts A & B it is recommended to degas the product to eliminate the air introduced in the mixture if the material is processed using an automatic dosing machine, each of the two parts has been previously degassed and air is not introduced during the mixing.
BLUESIL RTV 3542 A&B is degassed under a 30 to 50 mbar vacuum. When the vacuum is applied the product expands 3-4 times its initial volume and bubbles form on the surface. Once bubbles disappear, the mixture collapses back to its initial volume. To complete degassing simply wait few minutes before releasing the vacuum, the product will then be ready to use.
Remark: release the vacuum several times improves the degassing. For easier degassing only fill a recipient to 1/3 of its height.
Pour the degassed material slowly in a steady stream from one edge of the mould box so that the material flows evenly over the model minimizing the entrapment of air bubbles under the flowing rubber.

3. Cross linking
At room temperature (23°C) BLUESIL RTV 3542 A&B cures in approximately 24 hours regardless of the mould thickness. For best results the mould should be allowed to cure for additional 24 hours before using the moulds for production.
Room temperature curing assures the lowest possible shrinkage, if accelerated cure is desired, mild heat should be preferred. To minimize shrinkage cure the elastomer at maximum temperature of 60°C for 3-4 hours, higher temperatures will cause higher shrinkage.
Conversely at lower temperature polymerization is much slower, at 20°C 36 hours may be necessary to complete cross-linking.
Be aware that contact with certain materials can inhibit the curing of this RTV:

  • Natural rubbers vulcanized with sulphur
  • Polycondensation RTV catalysed with metal salts
  • PVC stabilizing agents
  • Amine cured epoxies
  • Sulphur containing clays.
In case of doubts it is recommendable to run a quick test with a small quantity of material in order to assess compatibility. Take note that cross contamination due to not well cleaned tools or devices is frequently the main causes of inhibition. The best way is to use only dedicated gear when processing polyaddition RTVs.

 

STORAGE t < +40°C IN ITS ORIGINAL PACKStore in a cool, dry place with adequate ventilation. Keep away from incompatible materials, open flames, and high temperatures. Store in tightly closed original container. equipped with a degassing device. Suitable containers: polyethylene. Steel drums coated with epoxy-resin.Please consult the Safety Data Sheet of this product.

BLUESIL RTV 3542 B TRANSLUCENT

BLUESIL RTV 3542 A&B is a two component, silicone elastomer which cures at room temperature by a polyaddition reaction (1:1 ratio).
Aiming at satisfying different application requirements, BLUESIL RTV 3542 A&B is available in 3 versions:

  • BLUESIL RTV 3542 A&B
  • BLUESIL RTV 3542 A&B HV (High Viscosity)
  • BLUESIL RTV 3542 A&B QC (Quick Curing)

2 Part RTV

Fluid

  • Excellent reproduction of details
  • Good mechanical properties
  • Low linear shrinkage
  • No release of toxic substances during and after curing
  • High resistance to inorganic chemicals and UV rays
  • Good release properties with organic resins and gypsum
  • High flowability for the standard and QC version or increased viscosity for the HV version
  • Possibility to choose longer (standard, HV version) or shorter working time (QC version)

This product is specifically formulated for the production of moulds for manufacturing copies in different materials (resins, gypsum, etc.) when high hardness and good elasticity are required. BLUESIL RTV 3542 A&B can be also used for the production of printing pads or printing rollers.

Asia Pacific;Europe Middle East Africa;Central and South America

For information about Storage and Shelf Life for this product, please download the Technical Data Sheet.

 Characteristics_A

 

 

ColorTranslucentPairedComp
Viscosity11000PairedCompRH 0174mPa.s

 Characteristics_B

 

 

ColorTranslucentPairedComp
Viscosity11000PairedCompRH 0174mPa.s

 

 

 Table_Characteristics_A_And_B

 

 

hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1Hardness41PairedMixRH 0110sh.A
pot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6apot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6aPot life30PairedMixRH 0114min

 

 

 

 

BLUESIL RTV 3542 A TRANSLUCENTBLUESIL RTV 3542 A TRANSLUCENT/our_offer/Product/90024774/90024775/BLUESIL-RTV-3542-A-TRANSLUCENT

 

 

 

 

 NeedAnExpert

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

 TDS

 

 

 

 

 

 

 SQUARE_NEWS_EVENT_PRODUCT